The aluminum-silicon refractory bricks are mainly used in preheaters, decomposing furnaces, tertiary air ducts, kiln door covers, grate coolers, cement rotary kiln decomposition zones and upper and lower transition zones.
The aluminum-silicon refractory bricks mainly include alkali-resistant refractory bricks, anti-stripping high allumina bricks, silica-mullite series refractory bricks and high-load soft phosphates bricks.
The physical and chemical indicators of the above mentioned bricks are as follows:
Refractory Name | Chemical Composition (Al2O3) % | C.C.S (MPa) | Alkali Resistance |
---|---|---|---|
Ordinary Alkali-Resistant Brick | 25~40 | ≥30 | I |
High-Strength Alkali-Resistant Brick | 25~40 | ≥60 | I |
Refractory Name | Chemical Composition % | Bulk Density (g/cm3) | Apparent Porosity (%) | CSS (MPa) |
Refractoriness Under Load (℃) (0.2MPa, T0.6) |
Thermal Shock Resistance (Cycle) (1100℃,water quenching) |
|
---|---|---|---|---|---|---|---|
Al2O3 | ZnO2 | ||||||
anti-stripping high allumina brick | ≥70 | ≥6.0 | ≥2.55 | ≤22 | ≥60 | ≥1470 | ≥20 |
≥70 | - | ≥2.55 | ≤20 | ≥60 | ≥1470 | ≥15 |
Refractory Name | Chemical Composition % | Bulk Density (g/cm3) | Apparent Porosity (%) | CSS (MPa) |
Refractoriness Under Load (℃) (0.2MPa, T0.6) |
Thermal Shock Resistance (Cycle) (1100℃,water quenching) |
Abrasion at Ambient Temperature (cm³) | |
---|---|---|---|---|---|---|---|---|
Al2O3 | SiO2+SiC | |||||||
silica-mullite series refractory brick | ≥65 | ≥30 | ≥2.60 | ≤19 | ≥85 | ≥1650 | ≥10 | ≤8 |
≥63 | ≥30 | ≥2.60 | ≤19 | ≥90 | ≥1600 | ≥10 | ≤8 | |
≥60 | ≥30 | ≥2.55 | ≤19 | ≥90 | ≥1550 | ≥12 | ≤8 | |
high abrasive brick | ≥50 | ≥30 | ≥2.50 | ≤17 | ≥90 | ≥1550 | ≥12 | ≤5 |
Tags: aluminum-silicon-refractory-brick, cement-rotary-kiln,
If you want to learn more about our Refractory Products, please feel free to fill the inquiry form below.
We will get in touch with you ASAP!
Copyright @ Zengzhou Rongsheng Kiln Refractory Co., Ltd. All Rights Reserved | Site Map | ExportBureau profile